RESUMO
Halide perovskites are excellent candidate materials for use in solar cell, LED, and detector devices, in part because their composition can be tuned to achieve ideal optoelectronic properties. Empirical efficiency optimisation has led the field towards compositions rich in FA (formamidinium) on the A-site and I on the X-site, with additional small amounts of MA (methylammonium) or Cs A-site cations and Br X-site anions. However, it is not clear how and why the specific compositions of alloyed, i.e., mixed component, halide perovskites relate to photo-stability of the materials. Here, we combine synchrotron grazing incidence wide-angle x-ray scattering, photoluminescence, high-resolution scanning electron diffraction measurements and theoretical modelling to reveal the links between material structure and photostability. Namely, we find that increased octahedral titling leads to improved photo-stability that is correlated with lower densities of performance-harming hexagonal polytype impurities. Our results uncover the structural signatures underpinning photo-stability and can therefore be used to make targeted changes to halide perovskites, bettering the commercial prospects of technologies based on these materials. This article is protected by copyright. All rights reserved.
RESUMO
2H-Benzotriazol-2-ylethylammonium bromide and iodide and its difluorinated derivatives are synthesized and employed as interlayers for passivation of formamidinium lead triiodide (FAPbI3) solar cells. In combination with PbI2 and PbBr2, these benzotriazole derivatives form two-dimensional (2D) Ruddlesden-Popper perovskites (RPPs) as evidenced by their crystal structures and thin film characteristics. When used to passivate n-i-p FAPbI3 solar cells, the power conversion efficiency improves from 20% to close to 22% by enhancing the open-circuit voltage. Quasi-Fermi level splitting experiments and scanning electron microscopy cathodoluminescence hyperspectral imaging reveal that passivation provides a reduced nonradiative recombination at the interface between the perovskite and hole transport layer. Photoluminescence spectroscopy, angle-resolved grazing-incidence wide-angle X-ray scattering, and depth profiling X-ray photoelectron spectroscopy studies of the 2D/three-dimensional (3D) interface between the benzotriazole RPP and FAPbI3 show that a nonuniform layer of 2D perovskites is enough to passivate defects, enhance charge extraction, and decrease nonradiative recombination.
RESUMO
Cross-sectional transmission electron microscopy has been widely used to investigate organic-inorganic hybrid halide perovskite-based optoelectronic devices. Electron-transparent specimens (lamellae) used in such studies are often prepared using focused ion beam (FIB) milling. However, the gallium ions used in FIB milling may severely degrade the structure and composition of halide perovskites in the lamellae, potentially invalidating studies performed on them. In this work, the close relationship between perovskite structure and luminescence is exploited to examine the structural quality of perovskite solar cell lamellae prepared by FIB milling. Through hyperspectral cathodoluminescence (CL) mapping, the perovskite layer was found to remain optically active with a slightly blue-shifted luminescence. This finding indicates that the perovskite structure is largely preserved upon the lamella fabrication process although some surface amorphisation occurred. Further changes in CL due to electron beam irradiation were also recorded, confirming that electron dose management is essential in electron microscopy studies of carefully prepared halide perovskite-based device lamellae. RESEARCH HIGHLIGHTS: Cathodoluminescence is used to study the emission of focused ion beam milled perovskite solar cell lamellae. The perovskite remained optically active with a slightly blue-shifted luminescence, indicating that the perovskite structure is mostly preserved.